@@ -462,12 +462,12 @@ \subsubsection{Terminology and  Definitions}
 \item \textit{Fully tempered (FT) glass -} A flat and monolithic, glass lite of 
 uniform thickness that has been subjected to a special heat treatment process 
 where the residual surface compression is not less than 69 MPa (10 000 psi) or 
-the edge compression not less than 67 MPa (9700 psi)as defined in \cite{ASTM2012}.
+the edge compression not less than 67 MPa (9700 psi)as defined in \cite{ASTM2012a}.
 
 \item \textit{Heat strengthened (HS) glass -} A flat, monolithic, glass lite of 
 uniform thickness that has been subjected to a special heat treatment process 
 where the residual surface compression is not less than 24 MPa (3500 psi) or 
-greater than 52 MPa (7500 psi)as defined in \cite{ASTM2012}.
+greater than 52 MPa (7500 psi)as defined in \cite{ASTM2012a}.
 
 \end{enumerate}